TEROSON EP 5055 - CARTRIDGE 250 ML
Teroson EP 5055 is a solvent free, two component adhesive, based on toughened Epoxy resins.
Characteristics
The material has a very good adhesion to e.g.:
- bare metal
- aluminum alloys
- zink coated steels
- E-coated panels
- By heating up both components the chemical reaction will accelerate
- Teroson EP 5055 will cure at room temperature
- Curing can be accelerated by increasing the temperature
- It is free of isocyanate and silicones. The cured adhesive film is hard, but not brittle
Application
It is special designed for bare steel, zinc coated steels and aluminum alloys used in the automotive industry or body repair shops, where high strenght and corrosion protection properties are required
Technical characteristics
Partie A
- Base : Epoxy Resin
- Colour : black
- Density : approx. 1,0 g/ml
- Viscosity : approx. 145 Pa.s
Measuring equipment : Physika UDS 200
Measuring system : plate/plate Ø 20 mm
Shear rate : 10 s-1
Temperature : 23°C
Partie B
- Base : Amine
- Colour :grey-green
- Density : approx. 1,1 g/ml
- Viscosity : approx. 75 Pa.s
Measuring equipment : Physika UDS 200
Measuring system : plate/plate Ø 20 mm
Shear rate : 10 s-1
Temperature : 23°C
- Mixing ratio A:B by volume : 1:1
Mixture (Part A+B)
- Colour : dark grey
- Odour : almost without odour
- Solids : 100%
- Curing times
initial strength : approx. 4 h at 23°C final strength : approx. 2 d at 23 °C or 30 minutes at 100 °C object temperature
- Shear strength (based on DIN EN 1465)
cured at ambient temperature : 18 à 22 MPa
cured at elevated temperature : > 20 MPa
- Peel test (DIN EN ISO 11339) :
Steel, 0.2 mm thick layer (7 d at 23 °C, 50 % rh) : > 4 N/mm
- E-Modulus : 1500 MPa
|