TEROSON MS 9220 BLACK - CARTRIDGE 310 ML
Teroson MS 9220 is a one component adhesive with high sag resistance, based on MS-Polymer.
Characteristics
- Cures by reaction with humidity to an elastic product
- The skin formation and curing times are dependent on humidity and temperature
- The curing time also depends on joint depth
- By increasing the temperature and humidity, the reaction time can be reduced
- Free of solvents, isocyanates, silicones and PVC
- Has only a weak odour (after curing it is odourless)
- Good adhesion to many substrates
- Good resistance to UV-light
Application
TEROSON MS 9220 is used in the areas :
- vehicle body manufature
- bus manufacture
- vehicle body build-ups
- caravan
- ship and boat building
Technical characteristics
- Colour : black
- Odour : odourless
- Consistancy : thixotropic paste
- Density : approx. 1,4 g/cm³
- Skin formation time* : approx. 6 min
- Tack-free time : approx. 20 to 30 min
- Cure rate : approx. 3,5 mm/24 h
- Shore-A-hardness (DIN 53505): approx. 60
- Tensile strength (acc. to DIN 53504) : approx. 3,3 MPa
- Tensile shear strength (DIN EN 1465) : 4,4 MPa
- Substrates: painted sheet metal
- Layer thickness : 0,2 mm
- Cross head speed : 10 mm/min
- Volume change (acc. to DIN 52451) : < 2%
- Application temperature : +15°C to +35°C
- In service temperature range : -40°C to +100°C
- Short exposure (up to 1 h) : +120°C
* DIN 50014 standard climate : 23°C, 50% relative air humidity
|