Teroson MS 9360 is a high viscosity, sag resistant one component adhesive based on silane modified polymer, which cures to an elastic product.
Characteristics
- The skin formation and curing times are dependent on humidity and temperature
- By increasing the temperature and moisture these times can be reduced
- Free of solvents, isocyanates and silicones.
- Good adhesion to many substrates
- Compatible with suitable paint systems
- Good UV resistance
Teroson MS 9360 allows accelerated curing as two-component material.
Application
Teroson MS 9360 is used for elastic bonding on metallic or painted substrates as well as for adhesive sealings of all kind. After matching of the materials to be bonded a high position tack is obtained
Technical characteristics
- Colour : black
- Odour : characteristic
- Consistancy : pasty, thixotropic
- Density : approx. 1,4 g/cm³
- Sag resistance : no sagging (DIN profile 15 mm)
- Shore-A-hardness (ISO 868, Durometer A): approx. 60
- Tensile strength (ISO 37) : approx. 3,5 MPa
- Elongation at break (ISO 37, speed 200 mm/min) : approx. 200%
- Stress at 100 % elongation (acc. to ISO 37) : approx. 2.0 MPa
- Volume change (acc. to DIN 52451) : < 2%
- Tensile shear strength (acc. to ISO 4587)*: 2.0 MPa
- Substrates: AlMg1SiCu, AlMg2.5
- Layer thickness : 2 mm
- Cross head speed : 10 mm/min
- UV resistance : no signif. changes
- UV source : Osram Vitalux 300W
- Distance to the specimen : 25 cm
- Test period : 6 weeks
- Application temperature : +5°C to +40°C
- In service temperature range : -40°C to +100°C
- Short exposure (up to 1 h) : +120°C
* ISO 291 standard climate : 23°C, 50% relative air humidity
|