TEROSON MS 9399 BLACK - CARTRIDGE 400 ML
Teroson MS 9399 is a highly viscous, sag-resistant, two-component adhesive based on silane-modified polymers, which cures independently of the atmospheric moisture to an elastic product.
Characteristics
- Free from solvents, iscoyanates and silicones
- UV resistant
- Good weathering resistance
Application
- Teroson MS 9399 can be used for elastic bondings, for example in the caravan manufacture, in the railroad vehicle industry or in shipbuilding.
Technical characteristics
Part A
- Density : approx. 1,4 g/cm³
Part B
- Density : approx. 1,3 g/cm³
Mixture (Part A + B)
- Colour : black
- Odour : characteristic
- Consistancy : thixotropic paste
- Density : approx. 1,35 g/cm³
- Sag resistance : jusqu'à 15 mm (profil DIN )
- Processing time / Open time 23°C : approx. 30 min
- Strength for further handling 23°C : approx. 2,5 to 3 h
- Shore-A-hardness (ISO 868, Durometer A)*: approx. 55
- Tensile strength (ISO 37) : approx. 3,0 MPa
- Elongation at break (ISO 37, speed 200 mm/min)* : approx. 150%
- Tensile shear strength (ISO 4587) : 2,0 MPa (métal ép. 1 mm)
- Substrates: Al 99.5
- Layer thickness : 2 mm
- Cross head speed : 10 mm/min
- UV resistance : no signif. changes
UV source : Osram Vitalux 300W
Distance to the specimen : 25 cm
Test period : 6 weeks
- Application temperature : +15°C to +40°C
- In service temperature range : -40°C to +100°C
- Short exposure (up to 1 h) : +120°C
* ISO 291 standard climate 23°C, 50% relative air humidity
|