TEROSON PU 8591T IN 600 ML CARTRIDGE

(Code: 02-20260-01)

Data Sheet
14.08 €
Add to cart
TEROSON PU 8591T IN 600 ML CARTRIDGE

TEROSON PU 8591T - CARTRIDGE 600 ML



Teroson PU 8591T is a 1-component polyurethane adhesive with excellent waethering stability.



Characteristics
The direct glazing adhesive is outstanding for the following properties:
  • Very good sag resistance
  • High cure rate
  • High elastic and shear strength, even after aging
  • Very low conductivity
  • Good adhesion to the remaining material
  • Excellent adhesion to glass, glass with the ceramic coating,encapsulation and to painted surfaces, in connection withprimer/activator
  • High UV resistance in connection with primer/activator


Application

Teroson PU 8591T is used for the bonding of front, rear and side screens to the body of motor-, utility-, special- and rail vehicles.
Bonding of side windows made of single–pane glass or insulating glass in bus and rail coach manufacture.
Teroson PU 8591T is also used as a gap filler with non staining properties.

Technical characteristics
  • Colour : black
  • Odour : weak
  • Consistency : smooth, sag-resistant, pasty
  • Density : approx. 1.27 g/cm3
  • Solids : 100%
  • Curing mechanism : humidity curing
  • Cure rate (DIN 50014 ; 23°C, 50% rh) : approx. 3 to 4 mm/24 hrs
  • Shore-A-hardness (DIN 53505): approx. 60
  • Tensile strength (DIN 53504): approx. 8.0 MPa
  • Stress (DIN 53504): approx. 2 MPa at 100 % elongation
  • Shear modulus (DIN 54451): approx. 2.0 MPa
  • Elongation at break (DIN 53504): approx. 400 %
  • Shear strength
        after 24h (DIN 54451) : 2.0 MPa
        Layer thickness 5 mm based on DIN 54451 : 5 to 6 MPa (fully cured)
  • Specific forward resistance (ASTM D 257-99 / DIN IEC 60093) : approx. 1×108 ω cm
  • Volume change (DIN 52451) : < 1 %
  • Glazing time* : approx. 20 mins
  • Material application temperature : +5°C to +35°C
  • Environmental temperature at application : -10°C to +45°C
  • In service temperature range : -40°C to +90°C
        short exposure (up to 1 hr.) : +120°C
* period of time between beginning of material application until inserting of the pane