TEROSON PU 9096 PL - CARTRIDGE 310 ML
Teroson PU 9096 PL is a 1 component moisture curing polyurethane adhesive.
Characteristics
Teroson PU 9096 PL demonstrates the following properties:
- Excellent adhesion without primer to glass, ceramic coated glass and on painted surfaces
- Good adhesion to primer
- Good adhesion to material residues and PUR pre-coatings
- High curing rate
- High UV resistance without primer
- High shear strength, retained on ageing
Application
Bonding of front, rear and side windows into the body of motor vehicles (cars, trucks, busses, driver cabins of tractors/fork lift trucks and special–purpose vehicles).
Bonding of side windows made of single–pane glass or insulating glass in bus and rail coach manufacture.
Technical characteristics
- Colour : black
- Odour : weak
- Consistency : smooth, sag-resistant paste
- Density : approx. 1.3 g/cm3
- Solids : 100%
- Curing mechanism : moisture curing
- Cure rate (DIN 50014 standard climate: 23°C, 50% rh) : approx. 4 mm/24 h
- Shore-A-hardness (DIN 53505) : approx. 60
- Tensile strength (DIN 53504) : approx. 7.5 MPa
- Stress (DIN 53504): approx. 2.7 MPa at 100 % elongation
- Shear modulus (based on DIN 54451) : approx. 1.2 MPa
- Elongation at break (DIN 53504) : approx. 350 %
- Shear strength (thickness 5 mm, based on DIN EN 1465) : 2 MPa (after 24 h DIN 50014)
5 - 6 MPa (fully cured)
- Volume change (DIN 52451) : < 1 %
- Glazing time : maximum 25 min. * standard climate
- Application temperature : +10°C to +35°C
- In service temperature range : -40°C to +90°C
short exposure (up to 1 h) : +120°C
* Period of time between beginning of material application until inserting of the pane |